3M™ Adhesive Transfer Tape with Plasticizer Resistant Adhesive F9465PC

General Information

Note: Vinyl formulations di er and plasticizer types and amounts can vary. The most common types of plasticized vinyl contain low molecular weight materials

(plasticizers) which tend to migrate out of the vinyl. In the case of adhesive bonding, these plasticizers migrate into the adhesive which can cause softening of the

adhesive and loss of bond strength over time.

• The possible e ect of plasticizer migration on an adhesive bond can be predicted by accelerated aging for 5 days at elevated temperature (150°F [65°C]). Note: Due

to the variability of vinyl formulations, we strongly recommend that the user test each vinyl substrate to determine suitability of the tape for the particular application.

• Natural and synthetic rubber materials such as neoprene and EPDM are also formulated with llers and plasticizers. Note: 3M™ Adhesive Transfer Tape F-9465PC

does not resist the e ects of these particular llers and plasticizers and is not recommended for use in bonding these materials.

Technical Information Note

The following technical information and data should be considered representative or typical only and should not be used for speci cation purposes.

Typical Physical Properties

Property

Values

Attribute Modi er

Notes

Adhesive Thickness

0.13 mm

5 mil

Liner

Polycoated Paper

Liner Color

Tan, printed

Primary

Liner Thickness

0.1 mm

4.2 mil

The thickness listed is based on a calculation

from manufacturing controlled adhesive coat

weights using a density of 1.012 g/cc. While past

data pages have listed nominal thicknesses, the

coat weight (and theoretical caliper) has not

changed.

Typical Performance Characteristics

Property Values

Test

Condition

Notes

Method

Dwell/Cure

Time

Dwell

Time

Units

Temp

C

Temp

F

Environmental

Condition

Substrate

Static

Shear

10000

min

500

g @

Room

Temperature

1/2 in x 1 in sample size; Test terminated at 10,000 min

180°

Peel

Adhesion

8.1

N/cm

74

oz/in

12 in/min (300 mm/min)

ASTM

D3330

72

hr

22C

72F

52%RH Stainless

Steel