3:1 Polyolefin Dual Wall

Heat Shrink Tubing, Clear

Newark.com/exclusive-brands

Farnell.com/exclusive-brands

Element14.com/exclusive-brands

Applications

Manufactured by co-extrusion of polyolefin and hot-melt adhesive. Designed to provide both insulation and sealing for protected

articles. Used to protect auto wires, shipping cable, bundle wires and metal tubes against water and moisture. High expansion

ratio makes it possible to repair most damaged cable jackets without removing connectors.

Features

• Operating temperature -45°C to +125°C

• Minimum shrink temperature 70°C

• Full recovery temperature 125°C

• Shrink Ratio 3:1

• Colour: Clear ( Transparent )

Technical Data - Out Jacket Material

Property

Test Method

Typical Data

Tensile Strength

ASTM D2671

≥12 Mpa

Ultimate Elongation

ASTM D 2671

≥300%

Longitudinal Shrinkage

UL 224

±8%

Heat Aging

Ultimate Elongation

158°C, 168hrs

≥200%

Flammability

VW-1

Pass (out jacket only)

Dielectric Strength

IEC 243

≥15kV/mm

Volume Resistivity

UL224

≥1014 Ω.cm

Copper Stability

ASTM D 2671

Pass

Copper Corrosion

UL224

No Corrosion

Property

Test Method

Typical Data

Water Absorption

ISO 62

<0.2%

Softening Point

ASTM D E28

95°C

Peel Strength (to PE)

ASTM D 1000

120N/25m

Peel Strength (to AL)

ASTM D 1000

80N/25m

Technical Data - Adhesive

Size

As supplied

After recovery

Inch

mm

Internal Diameter

Min. (mm)

Internal

Diameter Max.

Total Wall

Thickness

Wall Thickness

of Adhesive

1/8

3.2

3.2

1

0.9 ±0.3

0.35 ±0.2

3/16

4.8

4.8

1.6

1.05 ±0.3

0.4 ±0.2

1/4

6.4

6.4

2.2

1.25 ±0.3

0.45 ±0.2

5/16

7.9

7.9

2.7

1.3 ±0.3

0.45 ±0.2

Product Dimensions